It has fine multiple physical property with good low-temperature flexibility and better tearing strength. Its dissolved parameter are nearly same as PVC and it has good affinity with PVC. Under the condition of right processing, it can form a network composition inside of the hard PVC finish products and give them good normal, low-temperature flexibility and impact strength.
Specifications
- CPE135A
- Chlorine content % 35?
- Heat stable time ℃ ≥ 165
- Volatile Matter content % ≤0.3
- Remains crystallinity % ≤ 5
- Tearing Strength % ≥8.0
- Rete of filtration (36mesh) % ≥99
- Shore Hardness (A) ≤57
- Apparent Density g/ml ≥55
- Impurity Particle PC/ 50g < 10
- Whiteness(R457) ≥86
- CPE130A
- Chlorine content % 30?
- Remains crystallinity % ≤ 2
- Volatile Matter content % ≤0.3
- Residue on sieve 0.441mm bore diameter % ≤0.5
- 0.356mm bore diameter % ≤10
- Shore Hardness (A) ≤56
- Thermal decomposition temperature ℃ ≥165
- Mooney viscosity ML 65?
- Stretch hardness Mpa ≥7.5
- Elongation at break % ≥850
- CPE135B
- Chlorine content % 35?
- Remains crystallinity % ≤ 2
- Volatile Matter content % ≤0.3
- Fineness(26 mesh) % ≥99
- Shore Hardness (A) ≤55
- Thermal decomposition temperature ℃ ≥165
- Mooney viscosity ML 65?
- Stretch hardness Mpa ≥8.5
- Elongation at break % ≥850
- CPE1401
- Chlorine content % 40?
- Remains crystallinity % ≤ 2
- Volatile Matter content % ≤0.3
- Fineness(26 mesh) % ≥99
- Shore Hardness (A) ≤55
- Thermal decomposition temperature ℃ ≥165
- Mooney viscosity ML 70?
- Stretch hardness Mpa ≥8.5
- Elongation at break % ≥850
Features
- CPE135A
- It has fine multiple physical property with good low-temperature flexibility and better tearing strength. Its dissolved parameter are nearly same as PVC and it has good affinity with PVC. Under the condition of right processing, it can form a network composition inside of the hard PVC finish products and give them good normal, low-temperature flexibility and impact strength.
- CPE130A
- This product is a kind of Chlorinated Polyethylene Elastomer with high cold-resistance and high filling level. Besides the characteristics of common Chlorinated Polyethylene, it also has the characteristic of high toughness at low temperature, and excellent acceptance of high filler levels. Moreover it has good processing fluidity and good gloss on the surface of product after filled.
- CPE135B
- This product is a kind of amorphous elastomer with minimal crystal. It has lower Mooney viscosity and mastication temperature as well as excellent properties such as good processing property, excellent weathering resistance, good flex resistance and flame resistance. It can be blended with CR, CSM, NBR, EPDM, SBR and NR at any ratio. CPE1401
- It is a random and saturated thermoplastic elastomer with minimal residual crystal. It has excellent comprehensive physical properties such as very good flame-resistance, chemical-resistance, oil-resistance and waterproofing and also has good compatibility with PVC, CR etc.