Polyester metallized film: the extra low permeability for excellent barrier film purpose. Very high gloss of metallic with supreme appearance. Strong texture of pet film, high strength and stiffness.
Typical properties | Unit | Test methods | Typical value | Typical value |
---|---|---|---|---|
Thickness | Micron | Micrometer | 9 | 12 |
Yield | m^2/kg (min.) | N/A | 79 | 60 |
Average thickness variation | % (max.) | ASTM E-252-78 | +/-3 | +/-3 |
Tensile strength | kg/mm^2 (min.) MD/TD | ASTM D-882-83 | 17/18 | 17/18 |
Elongation at break | % (max.) MD/TD | ASTM D-882-83 | 140/120 | 140/120 |
Thermal shrinkage (150 Celsius 15 minutes) | % MD/TD | ASTM D-1204-84 | 2.0/1.5 | 2.0/1.5 |
C.O.F. | Film/film | ASTM D-1894 | 0.5 | 0.5 |
Optical density (OHM/SQ) | (max.) | N/A | 2.2 (2.05) | 2.2 (2.05) |
WVTR | g/m^2/24 hr (max.) | ASTM E-96 | 4 | 3 |
O(2)TR | cc/m^2/24 hr (max.) | ASTM D-1434 | 39 | 30 |
Corona treatment for one side | Dyne/cm (min.) | ASTM D-2578 | 50 | 50 |
Specifications
- Paper core I.D.: 76mm (3 in.) 152mm (6 in.)
- Roll O.D.: max. 600mm
- Width range: 100mm-2000mm (other width on request)
- Length range: standard 4000m., 6000m. (other width on request)
Features
- Product code: No. OP-101R1
- Further technical information on request
- Note: test aluminum bonding strength according to J.F. Hanlon, handbook of packaging engineering; section 18, test methods, under "bond or delamination" as a knife cut is made through one layer of substrate. Pressure sensitive tape is rubbed down across the cut. The tape is quickly pulled perpendicular to the surface. Any separation is reported as failure".